Pengaruh Interlayer Partikel Zn dengan Diameter Shoulder terhadap Struktur Mikro dan Sifat Mekanik Pengelasan Sambungan Friction Stir Spot Welding Alumunium AA1100

Author


Siska Irma Budianti(1Mail), Lingga Arti Saputra(2), Yonathan Ito(3),
(1) Universitas Perwira Purbalingga, Indonesia
(2) Universitas Perwira Purbalingga, Indonesia
(3) Universitas Perwira Purbalingga, Indonesia

Mail Corresponding Author
Article Analytic
  [File Size: 406KB]  Language: id
Available online: 2024-11-18  |  Published : 2024-11-18
Copyright (c) 2024 Siska Irma Budianti
Article can trace at:

Article Metrics

Abstract Views: 0 times PDF Downloaded: 0 times

Abstract


The purpose of this study is the effect of shoulder diameter with the addition of Zn particle interlayer on FSSW welding joints. The materials used are two aluminum plates with dimensions of 125 x 40 x 2 mm. The design of the FSSW welding specimen is in accordance with JIS G 3136. The results of the tensile test without Zn with the highest value at the tool diameter with a 14 mm pin of 29.8 MPa and the lowest value at the tool diameter with a 12 mm pin of 21 MPa. The tensile test results with Zn with the highest value at the tool diameter with a pin of 14 mm of 24.3 MPa and the lowest value at the tool diameter with a pin of 12 mm of 17.7 MPa. The specimen without Zn 61 HV is the area with the highest hardness value and the lowest hardness value without Zn 43 HV. While the specimen with 62 HV is the area with the highest hardness value and the lowest hardness value with Zn 42 HV.


Keywords


Aluminum; FSSW; Shoulder Diameter; Zn interlayer; Tensile Test

References


Ahmed, E., Muaz, M., Arif, S., Kant, R., Hamza, S. M., Alim, K., Khan, M. A., Khan, S. H., & Khan, S. H. (n.d.). Pr ep rin t n ot pe er re vie we d Pr t n ot pe ed.

Armansyah, Saedon, J., Ferdyanto, Toding Bunga, N., & Julian, J. (2022). Karakteristik Kekerasan Lasan Titik Gesekan dan Pengadukan pada Paduan Aluminium 5052-H112. Jurnal Asiimetrik: Jurnal Ilmiah Rekayasa & Inovasi, 4, 143–152. https://doi.org/10.35814/asiimetrik.v4i1.3183

Arti Saputra, L. (2023). Pengaruh Hybrid Interlayer Partikel Zinc Pada Friction Stir Spot Welding Material AA1100-AA5052. Rotasi, 25(3), 40–45.

Arti Saputra, L., & Ito, Y. (2023). Pengaruh Interlayer Elekroplating Cu Pada Mechanical Properties Sambungan FSSW Material AA6061-T6. Perwira Journal of Science & Engineering, 3(2), 46–47. https://doi.org/10.54199/pjse.v3i2.249

Arti Saputra, L., Muhayat, N., & Triyono, T. (2018). Effect of Zn Interlayer Particles on Mechanical Properties and Microstructure of Friction Stir Spot Welding Aluminum Alloy. MATEC Web of Conferences, 218, 1–6. https://doi.org/10.1051/matecconf/201821804005

Arumugam, A., & Pramanik, A. (2024). A Review on the Recent Trends in Forming Composite Joints Using Spot Welding Variants. Journal of Composites Science, 8(4). https://doi.org/10.3390/jcs8040155

Derbiszewski, B., Obraniak, A., Rylski, A., Siczek, K., & Wozniak, M. (2024). Studies on Quality of Joints and Phenomena Therein for Welded Vehicle Components Made of Aluminium Alloy – a Review. https://doi.org/10.20944/preprints202403.1458.v1

Dinari, M., & Haghighi, A. (2017). Surface modification of TiO2 nanoparticle by three dimensional silane coupling agent and preparation of polyamide/modified- TiO2 nanocomposites for removal of Cr (VI) from aqueous solutions. Progress in Organic Coatings, 110(April), 24–34. https://doi.org/10.1016/j.porgcoat.2017.04.044

Hu, T., Pan, H., Zhu, P., Zhou, J., Wu, T., Ding, K., & Gao, Y. (2024). Microstructure homogeneity and its role in the mechanical properties of the magnetic pulse welded steel/Al tubular joint. Journal of Materials Research and Technology, 30(March), 7076–7083. https://doi.org/10.1016/j.jmrt.2024.05.111

Kumar, A. H. S., Prasad, M. V. R. D., Narayan, Y. S., & Prakash, K. J. (2024). Experimental Analysis of Friction Stir Welding of Dissimilar Aluminium Alloys by Machine Learning. International Journal of Integrated Engineering, 16(2), 21–37. https://doi.org/10.30880/ijie.2024.16.02.003

Lukmanto, D., & Muhayat, N. (2020). Pengaruh Shoulder Plunge Depth Dan Panjang Pin Terhadap Sifat Fisik Dan Kekerasan Pada Sambungan Friction Stir Spot Welding Aluminium 1100 Dengan Penambahan Serbuk Zn. Jurnal Teknik Mesin Indonesia, 15(2), 13–20.

Natawiguna, C., Muhayat, N., & Triyono, T. (2018). Pengaruh Solution Heat Treatment terhadap Sifat Fisis dan Mekanik Proses Pengelasan Fssw AA6063-T5. Mekanika: Majalah Ilmiah Mekanika, 17(1). https://doi.org/10.20961/mekanika.v17i1.35044

Nugroho, A. W., Purnomo, F. H., & Rahman, M. B. N. (2021). Karakterisasi Sambungan Friction Stir Spot Welding pada Plat Aluminium 5083. Semesta Teknika, 24(1), 34–46. https://doi.org/10.18196/st.v24i1.12603

Saputra, L. A., Sukarno, N. A., & Zulaehah, S. (2021). Pengaruh Interlayer Elektroplating Zinc pada Kekuatan Mekanik Friction Stir Spot Welding Aa1100-Ss400. Semesta Teknika, 24(2), 93–101. https://doi.org/10.18196/st.v24i2.13015

Shakoori, A., Saeid, T., Ebrahimpour, A., & Faculty, E. (n.d.). Pr rin t n ot pe er r Pr ep rin t n ot pe er ed.

Singh, T., Tiwari, S. K., & Shukla, D. K. (2020). Mechanical and microstructural characterization of friction stir welded AA6061-T6 joints reinforced with nano-sized particles. Materials Characterization, 159(02). https://doi.org/10.1016/j.matchar.2019.110047


Refbacks

  • There are currently no refbacks.